Solef® 9007
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Solef® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ggY7Nv_Solef-9007.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Solef® 9007 PVDF homopolymer has low viscosity and is used in film extrusion and injection molding. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 to 1.80 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/3.8 kg | 16 to 26 | g/10 min | |
| 230°C/5.0 kg | 20 to 38 | g/10 min | |
| Molding Shrinkage - Flow | 2.0 to 3.0 | % | |
| Water Absorption (23°C, 24 hr) | < 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 1 sec, 2.00 mm) | 73 to 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C, 2.00 mm) | 1400 to 2200 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 23°C, 2.00 mm | 45.0 to 60.0 | MPa | |
| Break, 23°C, 2.00 mm | 30.0 to 50.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 23°C, 2.00 mm | 5.0 to 10 | % | |
| Break, 23°C, 2.00 mm | 20 to 300 | % | |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.15 to 0.35 | ||
| vs. Itself - Static | 0.20 to 0.40 | ||
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-10 Wheel) | 5.00 to 10.0 | mg | ASTM D4060 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 4(23°C, 4.00 mm) | 60.0 to 120 | J/m | ASTM D6110 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -40.0 | °C | ASTM D4065 |
| Melting Temperature | 162 to 168 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 133 to 140 | °C | ASTM D3418 |
| Crystallization Heat | 53.0 to 60.0 | J/g | ASTM D3418 |
| Heat of Fusion | 53.0 to 60.0 | J/g | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 20 to 25 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 kHz) | 7.00 to 10.0 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.100 mm) | V-0 | UL 94 | |
| Oxygen Index (3.00 mm) | 44 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | Type IV, 1.0 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 2 m/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax SV258 | LyondellBasell Industries | PP Impact Copolymer | Pro-fax |
| Jackdaw PP ER36BK8001 | Jackdaw Polymers | PP, Unspecified | Jackdaw PP |
| LUBAN™ 1102 MBF | Oman Oil Refineries & Petroleum Indistries Co. (Orpic) | PP Homopolymer | LUBAN™ |
| MAJORIS HFR200 | AD majoris | PP, Unspecified | MAJORIS |
| Hylex® P1303L2 HB | Entec Polymers | PC | Hylex® |