REPOL® H250FG
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | REPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ggR1FI_REPOL-H250FG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| REPOL Polypropylene H250FG is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific catalyst system. Repol H250FG is recommended for use in Fiber Spinning operations, for making multifilament yarn and staple fibre. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 34.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 11 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3 | 1650 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 25 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 104 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILENE® E6 K20VA V0 | Taro Plast S.p.A. | PP Copolymer | NILENE® |
| Mylar® EC (300 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| LNP™ THERMOTUF™ WF006N compound | SABIC Innovative Plastics Asia Pacific | PBT | LNP™ THERMOTUF™ |
| Plasmer 1080N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| Sylvin 9077-95LMW White 1457 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |