Cevian®-MAS MAS10, MAS10F
| Category: | MMS , Methyl Methacrylate Styrene |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Cevian®-MAS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ggNARW_Cevian--MAS-MAS10-MAS10F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cevian®-MAS MAS10, MAS10F is a Methyl Methacrylate Styrene (MMS) material. It is available in Asia Pacific. Primary attribute of Cevian®-MAS MAS10, MAS10F: Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.11 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 73 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 62.0 | MPa | ISO 527-2 |
| Flexural Modulus | 3300 | MPa | ISO 178 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 6.40 mm) | 15 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 12.7 mm | 87.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 77.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 90.0 | °C | ISO 306/B50 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Ball Pressure Test | 90 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 170 to 190 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 210 to 230 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 10.0 to 20.0 | MPa | |
| Screw Speed | 70 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G10 202 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| ZELAS® 7025 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | ZELAS® |
| CYCOLAC™ DL200H resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| Karina BLACK PVC COMPOUND 70900-48/1-E-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polene LDPE SU 1018 | TPI Polene Public Company Limited | LDPE | Polene LDPE |