Order Products : sales@su-jiao.com
CYCOLOY™ CY6414 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ggE6hu_CYCOLOYCY6414resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant modified PC using non-brominated and non-chlorinated flame retardant systems, offering high heat for application in appliances, lighting and electrical market. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 14 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2330 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 64.0 | MPa | ASTM D638 |
| Fracture | 62.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield 3 | 6.0 | % | ASTM D638 |
| Yield | 5.7 | % | ISO 527-2/50 |
| Fracture 4 | 85 | % | ASTM D638 |
| Fracture | > 100 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5 | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | ISO 179/1eA |
| 0°C | 17 | kJ/m² | ISO 179/1eA |
| 23°C | 28 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 220 | J/m | ASTM D256 |
| 0°C | 530 | J/m | ASTM D256 |
| 23°C | 800 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 118 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 134 | °C | ISO 306/B50 |
| -- | 135 | °C | ISO 306/B120 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C 6 | Pass | IEC 60695-10-2 | |
| 125°C | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.0E+16 | ohms | IEC 60093 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 3.01 | ASTM D150 | |
| 1 MHz | 2.95 | ASTM D150 | |
| Dissipation Factor | |||
| 1 kHz | 1.7E-3 | ASTM D150 | |
| 1 MHz | 8.8E-3 | ASTM D150, IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.20 mm | V-0 | UL 94 | |
| 2.50 mm | 5VB | UL 94 | |
| Glow Wire Flammability Index 7(0.750 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature 8 | IEC 60695-2-13 | ||
| 0.750 mm | 775 | °C | IEC 60695-2-13 |
| 1.50 mm | 775 | °C | IEC 60695-2-13 |
| 3.00 mm | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | 32 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 210 - 260 | °C | |
| Middle Temperature | 230 - 290 | °C | |
| Front Temperature | 240 - 300 | °C | |
| Nozzle Temperature | 230 - 290 | °C | |
| Processing (Melt) Temp | 250 - 300 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | 80*10*3 sp=62mm |
| 6 . | by VDE |
| 7 . | by VDE |
| 8 . | by VDE |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Roechling SUSTAPEI | Röchling Sustaplast SE & Co. KG | PEI | Roechling |
| Vydyne® R550H NT662 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Grilon® TSGZ-25/4 | EMS-GRIVORY | Nylon 66/6 | Grilon® |
| Hifax TRC 412P | LyondellBasell Industries | PP Alloy | Hifax |
| PALFORM® R C 09 | pal plast GmbH | Acetal (POM) Copolymer | PALFORM® |