LNP™ THERMOTUF™ VC006 compound
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gfti89_LNP-THERMOTUF-VC006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF VC006 is a compound based on Super Tough Nylon resin containing 30% Carbon Fiber. Added features of this material include: High Impact, Electrically Conductive. Also known as: LNP* THERMOTUF* Compound VC-1006 Product reorder name: VC006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.25 | % | |
| Across Flow : 24 hr | 1.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.62 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.95 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 20700 | MPa | ASTM D638 |
| -- | 19300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 197 | MPa | ASTM D638 |
| Yield | 193 | MPa | ISO 527-2/5 |
| Break 3 | 197 | MPa | ASTM D638 |
| Break | 193 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.9 | % | ASTM D638 |
| Yield | 2.9 | % | ISO 527-2/5 |
| Break 5 | 2.9 | % | ASTM D638 |
| Break | 2.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 15300 | MPa | ASTM D790 |
| -- 7 | 15500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 284 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 293 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 286 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 210 | J/m | ASTM D256 |
| 23°C 10 | 21 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 11 | 75 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 32.6 | J | ASTM D3763 |
| -- | 7.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 261 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 258 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 252 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 240 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.4E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.0E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 260 to 271 | °C | |
| Middle Temperature | 277 to 288 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 293 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ryton® R-7-120NA | Solvay Specialty Polymers | PPS | Ryton® |
| ASTAPET™ PC/PET MDA267 | Marplex Australia Pty. Ltd. | PET | ASTAPET™ |
| Evolue™-H SP50800P | Prime Polymer Co., Ltd. | HDPE | Evolue™-H |
| EPIGUM DPE/50 D | Crosspolimeri S.p.A. | TPV | EPIGUM |
| LNP™ STAT-KON™ CX99000 compound | SABIC Innovative Plastics Europe | PS (HIPS) | LNP™ STAT-KON™ |