Starex VE-1805
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gfslFq_Starex-VE-1805.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex VE-1805 is a High Impact Polystyrene product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20 mm | 0.20 to 0.60 | % | ASTM D955, ISO 2577 |
| Across Flow : 3.20 mm | 0.20 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 23.0 | MPa | ASTM D638 |
| Yield | 22.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 1800 | MPa | ASTM D790 |
| -- 3 | 1800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 29.0 | MPa | ASTM D790 |
| -- 5 | 32.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 98 | J/m | ASTM D256 |
| 23°C 7 | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 71.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 85.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 190 to 200 | °C | |
| Middle Temperature | 200 to 210 | °C | |
| Front Temperature | 210 to 220 | °C | |
| Nozzle Temperature | 220 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 20 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| 7 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuman PC SP910 | Shuman Plastics, Inc. | PC | Shuman PC |
| TULAMID® PA-SV30-LT2 | UCC Shchekinoazot | Nylon 6 | TULAMID® |
| Niche PA6BK | Niche Polymer, LLC | Nylon 6 | Niche |
| Generic PEK - Glass Fiber | Generic | PEK | Generic |
| Kangxi® FRABSMIV-0 | Wuxi Kangxi Plastics Technology Co.,Ltd. | ABS | Kangxi® |