Viprene™ G55A-32U-NAT
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Alliance Polymers & Services |
| Trademark: | Viprene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gfXD60_Viprene-G55A-32U-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Viprene™ G55A-32U-NAT is a UV and Heat Stabilized TPV (thermoplastic vulcanizate elastomer). This material can be easily procesed by extrusion or injection molding. It exhibits easy flowing characteristics. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.970 | g/cm³ | ISO 2781 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 55 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| 100% Strain | 1.90 | MPa | |
| 300% Strain | 3.00 | MPa | |
| Tensile Stress (Break) | 6.00 | MPa | ISO 37 |
| Tensile Elongation (Break) | 550 | % | ISO 37 |
| Tear Strength | 31 | kN/m | ISO 34-1 |
| Compression Set (70°C, 22 hr) | 33 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -60.0 | °C | ASTM D746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravamid® AGF40 BK45 | Ravago Group | Nylon 66 | Ravamid® |
| BESTNYL SI00VI12BWX | Triesa Plastics | Nylon 6 | BESTNYL |
| Celanex® 2300 GV1/50 | Celanese Corporation | PBT | Celanex® |
| ICORENE® PP CO14RM | ICO Polymers SA, A Division of A. Schulman | PP Copolymer | ICORENE® |
| LNP™ THERMOCOMP™ RF006LXP compound | SABIC Innovative Plastics Asia Pacific | Nylon 66 | LNP™ THERMOCOMP™ |