CYCOLAC™ MG94 resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gfQ48d_CYCOLACMG94resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Superior flow, injection molding ABS. Good impact. For thin-wall applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 39.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 - 0.70 | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.16 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 129 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 95.7 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 40.0 | MPa | ISO 527-2/5 |
| Yield | 45.0 | MPa | ISO 527-2/50 |
| Fracture | 35.0 | MPa | ISO 527-2/5, ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 2.0 | % | ISO 527-2/5 |
| Yield | 2.2 | % | ISO 527-2/50 |
| Fracture | 35 | % | ISO 527-2/5 |
| Fracture | 45 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2450 | MPa | ISO 178 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 23 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact 4 | ISO 180/1A | ||
| -30°C | 7.5 | kJ/m² | ISO 180/1A |
| 23°C | 18 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 100 mm span | 91.0 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 80.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 99.0 | °C | ISO 306/B50 |
| -- | 100 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 8.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 8.7E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (3.20 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 95.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 200 - 240 | °C | |
| Middle Temperature | 220 - 260 | °C | |
| Front Temperature | 220 - 260 | °C | |
| Nozzle Temperature | 210 - 250 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titalon® 5100CF | Titan Plastics Compounds Co., Ltd. | PC | Titalon® |
| XANTAR® SF 22 (Foamed) | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Forprene® 6NE001A70 | SO.F.TER. SPA | TPV | Forprene® |
| Kemcor LD 2203 | Qenos Pty Ltd | LDPE | Kemcor |
| NYLOY® AT-0060N | Nytex Composites Co., Ltd. | PS (GPPS) | NYLOY® |