EMERGE™ PC 8701HH
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gf7CHn_EMERGE-PC-8701HH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC 8701HH Advanced Resin is an ignition-resistant, glass reinforced, polycarbonate resin. This resin contains no bromine, chlorine, or phosphate additives. It is a medium flow PC resin with a mold release system, intended for injection molding applications. EMERGE ™ PC 8701HH has a UL 94 V-0 rating at 1.5 mm. Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4350 | MPa | ISO 527-2/50 |
| Tensile Stress (Yield) | 85.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 10 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 4100 | MPa | ISO 178 |
| Flexural Stress 2 | 139 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength (23°C) | 7.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 137 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 146 | °C | ISO 306/B50 |
| Ball Indentation Temperature | > 130 | °C | IEC 60598-1 |
| CLTE - Flow | 1.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity (2.00 mm) | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 70 | kV/mm | IEC 60243-1 |
| Dielectric Constant 3(2.00 mm) | 3.00 to 3.10 | IEC 60250 | |
| Dissipation Factor 4 | 8.0E-3 to 0.016 | IEC 60250 | |
| Comparative Tracking Index (3.00 mm, Solution A) | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 5(1.50 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index 6 | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature 7 | IEC 60695-2-13 | ||
| 1.00 mm | 850 | °C | |
| 2.00 mm | 850 | °C | |
| 3.00 mm | 850 | °C | |
| Oxygen Index 8 | 38 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 290 to 320 | °C | |
| Mold Temperature | 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 50 Hz to 1 MHz |
| 4 . | 50 Hz to 1 MHz |
| 5 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 6 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 7 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 8 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WanBlend® WHT-885ET8 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | WanBlend® |
| NEFTEKHIM ABS 0475E | Nizhnekamskneftekhim Inc. | ABS | NEFTEKHIM ABS |
| Niuk 50RN00 | Shanghai Niuk New Plastic Technology Co., Ltd. | Nylon 66 | Niuk |
| Bergamid™ B70 G40 H UV BK043 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| INSPIRE™ TF4700SZ | Trinseo | PP, Unspecified | INSPIRE™ |