INELEC PA610CF30
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INELEC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gewidr_INELEC-PA610CF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Specific Volume | 0.814 | cm³/g | |
| Molding Shrinkage - Flow | 0.20 to 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 193 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.0 to 4.0 | % | ASTM D638 |
| Flexural Modulus | 15200 | MPa | ASTM D790 |
| Flexural Strength | 279 | MPa | ASTM D790 |
| Shear Strength | 82.7 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 750 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 257 | °C | ASTM D648 |
| CLTE - Flow | 1.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 238 to 274 | °C | |
| Mold Temperature | 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.013 to 0.025 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDM 540 | Marco Polo International, Inc. | HDPE | MARPOL® |
| Moplen HP648T | LyondellBasell Industries | PP Homopolymer | Moplen |
| Hax™ HF 211 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| SCHULABLEND® (ASA/PA) M/MW 6201 MT | A. Schulman Europe | ASA+Nylon | SCHULABLEND® |
| Sylvin 916VO NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |