ARLEN™ C215
| Category: | Nylon 6T , Polyamide 6T |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | ARLEN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | getsci_ARLEN-C215.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ARLEN™C215 is a polyamide 6T (nylon 6T) material, which contains a 15% glass fiber reinforced material. This product is available in North America,. ARLEN™The main characteristics of C215 are: flame retardant/rated flame. ARLEN™The typical application areas of C215 are: electrical/electronic applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.30 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow : 2.00mm | 0.60 | -- | % | ASTM D955 |
| Transverse flow : 2.00mm | 0.90 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 0.40 | -- | % | ASTM D570 |
| 100°C, 24 hr | 3.8 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (M-Scale) | 105 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 110 | 90.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 3.0 | % | ASTM D638 |
| Flexural Modulus | 6000 | 4000 | MPa | ASTM D790 |
| Flexural Strength | 180 | 150 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 50 | 55 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 295 | -- | °C | ASTM D648 |
| Glass Transition Temperature | 85.0 | -- | °C | DSC |
| Melting Temperature | 310 | -- | °C | |
| Linear thermal expansion coefficient | ASTM D696 | |||
| Flow | 3.4E-5 | -- | cm/cm/°C | ASTM D696 |
| Lateral | 5.5E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+16 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength | 25 | -- | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.20 | -- | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.020 | -- | ASTM D150 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 - 6.0 | hr | |
| Hopper Temperature | 50.0 - 90.0 | °C | |
| Rear Temperature | 300 - 325 | °C | |
| Middle Temperature | 315 - 335 | °C | |
| Front Temperature | 320 - 335 | °C | |
| Nozzle Temperature | 315 - 335 | °C | |
| Mold Temperature | 90.0 - 140 | °C | |
| Injection Rate | Moderate | ||
| Screw Speed | 150 | rpm |
| Injection instructions |
|---|
| Injection Pressure: Medium Pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 SI | RTP Company | Acetal (POM) Copolymer | RTP |
| TECAFORM® UD Blue | Ensinger Inc. | Acetal (POM) Copolymer | TECAFORM® |
| Vi-Chem PVC V141-60I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Desmovit® DP R 9918 | geba Kunststoffcompounds GmbH | TPU-Ester/Ether | Desmovit® |
| Karina WHITE COLOR CONCENTRATE 10/ 96-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |