Lucky Enpla LMF6200
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Lucky Enpla Co LTD |
| Trademark: | Lucky Enpla |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ger8y0_Lucky-Enpla-LMF6200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lucky Enpla LMF6200 is a polypropylene product that contains 20% mineral fillers. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. Lucky Enpla LMF6200 applications include electrical/electronic applications and the automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.90 - 1.4 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 32.4 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2750 | MPa | ASTM D790 |
| Flexural Strength 3 | 44.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (6.35 mm) | 29 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 135 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 200 - 220 | °C | |
| Middle Temperature | 200 - 220 | °C | |
| Front Temperature | 210 - 230 | °C | |
| Nozzle Temperature | 210 - 230 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Back Pressure | 0.490 - 1.47 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Resin Temperature: 210-230°CInjection Pressure (1st Pressure): 500-800 kg/cm²Injection Pressure (2nd Pressure): 300-600 kg/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 30 mm/min |
| 3 . | 30 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT GP2307FI | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| Moplen HP400K | LyondellBasell Industries | PP Homopolymer | Moplen |
| Xuchuan 1001A/B-5301 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyether | Xuchuan |
| Kinta NI6600 | Kinta Technology (Hong Kong) Co., Ltd. | Nylon 66 | Kinta |
| LNP™ LUBRICOMP™ LCL33 compound | SABIC Innovative Plastics | PEEK | LNP™ LUBRICOMP™ |