TECHNYL® A 218 MZ15 V25 BLACK 31 N
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | geoqqc_TECHNYL-A-218-MZ15-V25-BLACK-31-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 218 MZ15 V25 Black 31 N is a polyamide 66, reinforced with 25% of glass fibre and 15% of mineral filler, heat stabilized, for injection moulding. This product is available in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.47 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.66 | -- | % | |
| Water Absorption (23°C, 24 hr) | 1.0 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.650 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 7500 | MPa | ISO 527-2/1A |
| Tensile Strength | ||||
| Break | 150 | -- | MPa | ASTM D638 |
| Break | 140 | 115 | MPa | ISO 527-2/1A |
| Tensile Elongation | ||||
| Break | 2.0 | -- | % | ASTM D638 |
| Break | 2.0 | 3.0 | % | ISO 527-2/1A |
| Flexural Modulus | ||||
| -- | 9600 | -- | MPa | ASTM D790 |
| -- | 9000 | -- | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 220 | -- | MPa | ASTM D790 |
| -- | 210 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 45 | 55 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| 23°C | 70 | -- | J/m | ASTM D256 |
| 23°C | 4.0 | 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 240 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PC PC1500 resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |
| ISOTHANE® G1085A-E | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |
| Hostacom M4 U42 LW92607 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| ALCOM® LD2 PC 1000 14050 GY1118-14 | ALBIS PLASTIC GmbH | PC | ALCOM® LD2 PC |
| POCAN® A 3121 000000 | LANXESS GmbH | PBT+ASA | POCAN® |