HI-ZEX™ 550P
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Prime Polymer Co., Ltd. |
| Trademark: | HI-ZEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gec7el_HI-ZEX-550P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HI-ZEX™550P is a high-density polyethylene product,. It can be processed by pipeline extrusion molding or extrusion, and is available in North America, Europe or Asia Pacific. Typical application areas are: water pipes/pipes/drinking water. The main characteristics are: high resistance to environmental stress fracture (escr). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.946 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.23 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (Compression Molded) | > 1000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Rotational Molded) | 950 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 23.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Compression Molded) | 300 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 1100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (Compression Molded) | 20 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 122 | °C | ISO 306 |
| Melting Temperature (DSC) | 131 | °C | ISO 3146 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357-3Tensile Strain at Break, ISO 527: >300% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TITANZEX® HB6200 | Lotte Chemical Titan (M) Sdn. Bhd. | HDPE | TITANZEX® |
| APEX® 3300-65NT | Teknor Apex Company | PVC, Flexible | APEX® |
| ELITE™ NG 5400B | The Dow Chemical Company | EPE | ELITE™ |
| Karina BLACK PVC COMPOUND TR-601D48/1-Y-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8940-70HMW Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |