| CAPRAN MEDALLION® 800 is a 0.32 mil (8 micron) biaxially oriented nylon 6 film with superior flex crack resistance and clarity properties well suited for packaging applications requiring excellent mechanical strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With Metal-Dynamic | 0.17 | ASTM D1894 | |
| With self-dynamics | 0.44 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 8.1 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 8.1 µm | 2760 | MPa | ASTM D882 |
| TD : 8.1 µm | 1900 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 8.1 µm | 241 | MPa | ASTM D882 |
| TD : Fracture, 8.1 µm | 290 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 8.1 µm | 90 | % | ASTM D882 |
| TD : Fracture, 8.1 µm | 75 | % | ASTM D882 |
| Oxygen Permeability (25°C, 8.1 µm) | 2.1 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (8.0 µm, 38°C, 100% RH) | 530 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 8.13 µm) | 150 | ASTM D2457 | |
| Haze (8.13 µm) | 2.5 | % | ASTM D1003 |
| Additional Information |
|---|
| Yield: 75500 in²/lbGraves Tear (initial), ASTM D 1004, MD: 1100 g/milGraves Tear (initial), ASTM D 1004, TD: 1100 g/milSurface Tension, ASTM D5946, treated side: >/= 56 dynes/cmSurface Tension, ASTM D5946, untreated side: >50 dynes/cmDimensional Stability, ASTM D1204, MD, 320°F, 5min: 2.5% shrinkageDimensional Stability, ASTM D1204, TD, 320°F, 5min: 1.5% shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® STR 3035EU-01 NATURAL | A. Schulman Inc. | Polyolefin, Enhanced (Capstock Resin) | POLYTROPE® |
| Nilac TBA/V | Soredi S.p.a. | ABS | Nilac |
| Elastron® G G101.A90.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Hostacom TRC 364NA | LyondellBasell Industries | TPO (POE) | Hostacom |
| ISOTHANE® GB1095A-H | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |