Order Products : sales@su-jiao.com
OP - PPO PPOX-10GF
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - PPO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gdtmr2_OP---PPO-PPOX-10GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OP-PPO PPOX-10GF is a polyphenylene ether + PS (PPE + PS) material, and its filler is 10% glass fiber reinforced material. This product is available in North America and is processed by injection molding. The main characteristics of OP-PPO PPOX-10GF are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (315°C/5.0 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 72.4 | MPa | ASTM D638 |
| Fracture | 72.4 | MPa | ASTM D638 |
| Flexural Modulus | 3450 | MPa | ASTM D790 |
| Flexural Strength | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 127 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 121 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | UL 94 | |
| 3.18 mm | HB | UL 94 |
| Additional Information |
|---|
| Melt Mass -Flow Rate (MFR), ASTM D1238, 315°C/ 5.0kg: 2 to 6 g/10 min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 260 - 304 | °C | |
| Middle Temperature | 271 - 310 | °C | |
| Front Temperature | 282 - 316 | °C | |
| Processing (Melt) Temp | 288 - 316 | °C | |
| Mold Temperature | 71.1 - 104 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® MB 3000 NAT | Arkema | Nylon 11 | Rilsan® |
| SUMILITE® EL-3800F | Sumitomo Bakelite Co., Ltd. | Epoxy | SUMILITE® |
| BLUESTAR® PBT 403M-G20 | Nantong Zhonglan Engineering Plastics Co., Ltd. | PBT | BLUESTAR® |
| Generic PPS - Organic | Generic | PPS | Generic |
| Karina GRAY PVC COMPOUND 801-18/489-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |