RTP 803 CC GB 20
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gctp49_RTP-803-CC-GB-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. RTP 803 CC GB 20 is a glass fiber and glass bead reinforced acetal designed for strength and dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8960 | MPa | ASTM D638 |
| Tensile Strength | 103 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 7580 | MPa | ASTM D790 |
| Flexural Strength | 152 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 166 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 163 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 5mil/in. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 191 - 210 | °C | |
| Middle Temperature | 191 - 210 | °C | |
| Front Temperature | 191 - 210 | °C | |
| Mold Temperature | 93.3 - 121 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Back Pressure | 0.172 - 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ 2010 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Dutral® TER 4437 WO | Versalis S.p.A. | EPDM | Dutral® |
| Karina WHITE PVC COMPOUND 837-10/ 37-A-ERYB-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SD POLYCA™ IM-401-18 | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |
| LG ASA LI980 | LG Chem Ltd. | ASA | LG ASA |