Westlake LF2020 is a hexene LLDPE with excellent physical properties and heat sealing characteristics, which allow for down-gauging and blending with other materials. Typical applications include stretch films, heavy duty bags and sacks, agricultural films, and trash bags & liners. This material is a available with various slip and antiblock levels. Application/Uses: Bags and sacks Agricultural films Trash bags and line Co-extruded structures |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 207 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 248 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 40.7 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 28.3 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 670 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 900 | % | ASTM D882 |
| Dart Drop Impact 4(25 µm, Blown Film) | 220 | g | ASTM D1709A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (25.4 µm, Blown Film) | 15 | % | ASTM D1003 |
| Additional Information |
|---|
| Test specimens for blown film: nominal thickness 1.0 mils fabricated at 2.5:1 BUR. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 204 - 216 | °C |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BB3X | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| Asaflex™ 815 | AKelastomers | SBS | Asaflex™ |
| Devcon Carbide Putty | Devcon | Epoxy | Devcon |
| ISPLEN® PB 171 H | REPSOL | PP Impact Copolymer | ISPLEN® |
| Polyrocks 5003G15H | Polyrocks Chemical Co., Ltd | PP, Unspecified | Polyrocks |