Alathon® H5618
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gcggsM_Alathon-H5618.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALATHON H5618 provides easy processing characteristics and exhibits excellent toughness properties and color as well as low odor and good processing stability. Typical applications include housewares, containers, caps and closures. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.53 to 0.59 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Spiral Flow | 29.7 | cm | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 69 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- | 1050 | MPa | |
| 1% Secant | 845 | MPa | |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 29.2 | MPa | |
| Break | 24.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 8.0 | % | |
| Break | 62 | % | |
| Flexural Modulus 4 | ASTM D790 | ||
| -- | 1490 | MPa | |
| 1% Secant | 1410 | MPa | |
| 2% Secant | 1180 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 31 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 72.8 | °C | ASTM D648 |
| Brittleness Temperature | < -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 |
| Peak Melting Temperature | 130 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 115 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYCOA Polyamide 1047 | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Elastron® G G101.A73.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Karina WHITE PVC COMPOUND 653D10/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ LF008 compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |
| OnFlex™ V 3050D-S0097 | PolyOne Corporation | TPE | OnFlex™ |