LNP™ LUBRICOMP™ 9X06084 compound
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gcRLVy_LNP-LUBRICOMP-9X06084-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP 9X06084 is a compound based on PA46 resin containing PTFE. Added features include: Internally Lubricated, Heat Stabilized. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 2.1 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 84.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 13 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2500 | MPa | ISO 178 |
| Flexural Stress | 103 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 95 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 247 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 77.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 299 to 310 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 310 to 321 | °C | |
| Mold Temperature | 82.2 to 121 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Crastin® CE2055 BK580 | DuPont Performance Polymers | PBT | Crastin® |
| Encapso® K | Smooth-On, Inc | Rubber | Encapso® |
| HiFill® PBT 0150 S | Techmer Engineered Solutions | PBT | HiFill® |
| Axiall PVC 8897 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| SABIC® LDPE PCG00 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |