LNP™ LUBRICOMP™ QCL34 compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gcLw23_LNP-LUBRICOMP-QCL34-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP QCL34 is a compound based on Nylon 6/10 resin containing 15% PTFE, 20% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive. Also known as: LNP* LUBRICOMP* Compound QCL-4034 Product reorder name: QCL34 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.060 to 0.080 | % | |
| Across Flow : 24 hr | 0.40 to 0.60 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.19 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 16600 | MPa | ASTM D638 |
| -- | 15600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 201 | MPa | ASTM D638 |
| Break | 197 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.7 | % | ASTM D638 |
| Break | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 12400 | MPa | ASTM D790 |
| -- 5 | 12500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 280 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 289 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 288 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.39 | ||
| vs. Itself - Static | 0.33 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.300 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 26.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C 8 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 840 | J/m | ASTM D4812 |
| 23°C 9 | 53 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 10.0 | J | ASTM D3763 |
| -- | 3.58 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 221 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 212 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 206 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.8E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*3 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000 GVS 10/20 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| YUNGSOX® PP 5250T | Formosa Polypropylene | PP Random Copolymer | YUNGSOX® PP |
| DuraGrip® DGR 6850NC | Advanced Polymer Alloys | TPE | DuraGrip® |
| Karina CLEAR PVC COMPOUND -E 75/161-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucet® N145-LD | LG Chem Ltd. | Acetal (POM) Copolymer | Lucet® |