PPS-hFR42 is filled PPS compound, which is filled with mineral based on the PPS resin. It shows high rigidity, creep resistance, high-temperature resistance, inherent flame resistance, chemical resistance, excellent electrical insulation properties, arc resistance, low water absorption, easy processing, low mold shrinkage, good dimensional stability, and radiation resistance. Its colour is offwhite. Owing to its high performance and light colour, it's an excellent selection for outer decorating parts with high temperature resistance and high rigidity in electronic/electric and medical industry. Such as: outer shells of apparatus and electric appliance, connectors, high-temperature disinfectant instruments, surgical containers, shells of the electric tooth-cleaning devices and other devices used in dentistry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.78 | g/cm³ | Internal method |
| Molding Shrinkage - Flow | 0.25 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 105 | MPa | Internal method |
| Tensile Elongation (Break) | 1.7 | % | Internal method |
| Flexural Modulus | 15200 | MPa | Internal method |
| Flexural Strength | 167 | MPa | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 5.7 | kJ/m² | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 214 | °C | Internal method |
| Melting Temperature | 282 | °C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.3E+15 | ohms | Internal method |
| Volume Resistivity | 1.0E+17 | ohms·cm | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 300 - 320 | °C | |
| Front Temperature | 300 - 320 | °C | |
| Nozzle Temperature | 290 - 320 | °C | |
| Processing (Melt) Temp | 160 - 180 | °C | |
| Mold Temperature | 100 - 150 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Back Pressure | 0.100 - 1.00 | MPa | |
| Screw Speed | 40 - 100 | rpm |
| Injection instructions |
|---|
| Processing time: 4 to 8hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RANPELEN J-560K | Lotte Chemical Corporation | PP Random Copolymer | RANPELEN |
| APEX® 3211-55NT | Teknor Apex Company | PVC, Flexible | APEX® |
| ChronoThane™ T 93A-B20 | AdvanSource Biomaterials Corp. | TPU-Polyether | ChronoThane™ |
| ENGAGE™ 8452 EL | The Dow Chemical Company | TPO (POE) | ENGAGE™ |
| KMI PBS KM804 | KMI Group Inc. | PBS | KMI PBS |