Fiberfil® J-61/20/E
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gbLVPg_Fiberfil-J-61-20-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil®J-61/20/E is a polypropylene copolymer (PP Copoly) material, which contains a 20% glass fiber reinforced material. This product is available in North America,. Fiberfil®The main features of J-61/20/E are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.20 - 0.30 | % | ASTM D955 |
| 6.35 mm | 0.30 - 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3240 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 48.3 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 3100 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 65.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 141 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 135 | °C | ASTM D648 |
| Additional Information |
|---|
| Rockwell Hardness, ASTM D785, R-Scale: 100 to 110 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silplus® 60 CW | Momentive Performance Materials Inc. | Silicone Rubber, HTV | Silplus® |
| TORZEN® G4000HSL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Bergamid™ A700 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| LNP™ STAT-KON™ DD200C compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |
| Sylvin 8784-77 Black 280 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |