ADVANCENE™ EE-4811-AAH
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | ETHYDCO |
| Trademark: | ADVANCENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gbCYV4_ADVANCENEEE4811AAH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADVANCENE™ EE-4811-AAH High Density Polyethylene Resin is a high molecular weight, high-density polyethylene copolymer that has been designed specically for tubular film extrusion. Its broad molecular weight distribution and density successfully combine excellent performance at high extrusion rates with high film strength and rigidity. Tubular films of ADVANCENE™ EE-4811-AAH Resin are recommended for high strength grocery sacks. shopping bags and notion and millinery bags. The excellent drawdown characteristic of this product permits production of high-quality thin films for multiwall sack liners and replacements for thin paper products. The combination of strength and drawdown makes this resin ideal for downgauging in many applications. Films are readily treated and printed to give high-quality graphics. ADVANCENE™ EE-4011-AAH Resin is compatible with color concentrates, thus permitting the production of a variety of colored films that serve as protective and attractive decorative wraps. Main Characteristics:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.948 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 11 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus - 1% Secant | 814 | MPa | ASTM D790, ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 13 | µm | |
| Film Puncture Energy 1 | 1.20 | J | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 13 µm | 27.6 | MPa | ASTM D882 |
| TD : Yield, 13 µm | 24.1 | MPa | ASTM D882 |
| MD : Broken, 13 µm | 55.2 | MPa | ASTM D882 |
| TD : Broken, 13 µm | 53.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 13 µm | 270 | % | ASTM D882 |
| TD : Broken, 13 µm | 350 | % | ASTM D882 |
| Dart Drop Impact (13 µm) | 150 | g | ASTM D1709A, ISO 7765-1 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 13 µm 2 | 70 | g | ASTM D1922 |
| TD : 13 µm | 150 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 124 | °C | ASTM D1525, ISO 306 |
| Peak Melting Temperature | 132 | °C | ASTM D3418, ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 216 | °C |
| Note Message | |
|---|---|
| 1 . | Univation Method |
| 2 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRISTAR® PC-10R-CL(22) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| Bayflex® MP-25000 | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| EMOPLEN® CP MTF 25 UV | EMAS Plastik San.Tic.AS. | PP Copolymer | EMOPLEN® |
| Novamid® N-X150 | DSM Engineering Plastics | Nylon 6+Nylon 66/6 | Novamid® |
| GELOY™ CR7020 resin | SABIC Innovative Plastics | ASA | GELOY™ |