Hostacom G2 U02 102297
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gZv9yA_Hostacom-G2-U02-102297.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| "Hostacom" G2 U02 102297 (not specified black) is a 20% glass fiber coupled PP homopolymer with high flow, high stiffness, low creep under load at elevated temperatures. It is not intended for medical, pharmaceutical or drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.25 to 0.95 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 104 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 4600 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 72.0 | MPa | |
| Break | 75.0 | MPa | |
| Tensile Strain (Break) | 3.4 | % | ISO 527-2 |
| Flexural Modulus - Secant 1(23°C) | 4000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Hinged Break) | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C, Hinged Break) | 38 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 133 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pomalux® CN-SS | Westlake Plastics Company | Acetal (POM) Copolymer | Pomalux® |
| NORYL™ PX9406K resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| Fluon® PTFE RA7003 | Asahi Glass Co., Ltd. | PTFE | Fluon® |
| Lupoy® GN2301F | LG Chem Ltd. | PC | Lupoy® |
| Sylvin 8739-65FU White 1394 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |