ENGAGE™ 8180 Polyolefin Elastomer is a lower density, high performance ethylene-octene copolymer that has excellent flow characteristics and provides superb impact properties in blends with polypropylene (PP) and polyethylene (PE). It is widely used in TPO applications where excellent flow temperature impact properties are desired.

ENGAGE 8180 also provides high filler loading capability and excellent electrical properties. When cross-linked by peroxide, silane, or irradiation, it gives exceptional heat aging, compression set, and weather resistance properties.

Main Characteristics:

Pellet form

Excellent flow characteristics

Improved impact in polypropylene and polyethylene

High filler loading

Peroxide, silane, and radiation curable

Exceptional heat aging, compression set, and weather resistance when cured

Applications:

General purpose thermoplastic elastomers

Impact modification

Thermoplastic olefins (TPO)

Wire and cable

Complies with:

EU, No 10/2011

U.S. FDA 177.1520(c)3.2c

U.S. FDA DMF

Consult the regulations for complete details.

General Information
Agency Ratings	DMF Unspecified Rating EU No 10/2011 FDA 21 CFR 177.1520(c) 3.2c
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.863	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.50	g/10 min	ASTM D1238
Mooney Viscosity (ML 1+4, 121°C)	37	MU	ASTM D1646

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness			ASTM D2240
Shore A, 1 sec, Compression Molded	63
Shore D, 1 sec, Compression Molded	16

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus - 100% Secant ¹(Compression Molded)	1.90	MPa	ASTM D638
Tensile Strength ²(Break, Compression Molded)	6.30	MPa	ASTM D638
Tensile Elongation ³(Break, Compression Molded)	910	%	ASTM D638
Flexural Modulus			ASTM D790
1% Secant : Compression Molded	8.50	MPa
2% Secant : Compression Molded	7.70	MPa

Elastomers	Nominal Value	Unit	Test Method
Tear Strength ⁴	32.0	kN/m	ASTM D624

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	-55.0	°C	Internal Method
Vicat Softening Temperature	41.0	°C	ASTM D1525
Melting Temperature (DSC) ⁵	47.0	°C	Internal Method
Peak Crystallization Temperature (DSC)	32.0	°C	Internal Method

Note Message
1 .	510 mm/min
2 .	510 mm/min
3 .	510 mm/min
4 .	Die C
5 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
Ultradur® B 4300 G6	BASF Corporation	PBT	Ultradur®
APEX® RM 8000R1-NT	Teknor Apex Company	PVC, Rigid	APEX®
ESTAPROP K1060 GFC/M	Cossa Polimeri S.r.l.	PP Copolymer	ESTAPROP
Hanwha Total PP TB53	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP, High Crystal	Hanwha Total PP
Infino XK-2307	SAMSUNG SDI CO., LTD.	PPS	Infino