| Monprene CP-18143 CLR is a clear thermoplastic elastomer designed for a variety of consumer product applications requiring a soft, rubber-like feel. Monprene CP-18143 CLR is a low hardness. low specific gravity grade that exhibits high flow characteristics, suitable for injection molding and extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.878 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 second, injection molding | 42 | ASTM D2240 | |
| Shore A, 5 seconds, injection molding | 40 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain 1 | 7.30 | MPa | ASTM D412 |
| Flow : 100% strain 2 | 5.92 | MPa | ASTM D412 |
| Transverse flow : 300% strain 3 | 1.90 | MPa | ASTM D412 |
| Flow : 300% strain 4 | 2.31 | MPa | ASTM D412 |
| Tensile Strength 5 | ASTM D412 | ||
| Transverse flow : Fracture | 6.49 | MPa | ASTM D412 |
| Flow : Fracture | 7.13 | MPa | ASTM D412 |
| Tensile Elongation 6 | ASTM D412 | ||
| Transverse flow : Fracture | 590 | % | ASTM D412 |
| Flow : Fracture | 690 | % | ASTM D412 |
| Tear Strength 7 | ASTM D624 | ||
| Transverse flow | 23.1 | kN/m | ASTM D624 |
| Flow | 24.2 | kN/m | ASTM D624 |
| Compression Set 8(23°C, 22 hr) | 16 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 182 - 232 | °C | |
| Middle Temperature | 188 - 238 | °C | |
| Front Temperature | 193 - 243 | °C | |
| Nozzle Temperature | 199 - 249 | °C | |
| Processing (Melt) Temp | 199 - 249 | °C | |
| Mold Temperature | 35.0 - 48.9 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 182 - 232 | °C | |
| Cylinder Zone 2 Temp. | 188 - 238 | °C | |
| Cylinder Zone 3 Temp. | 193 - 243 | °C | |
| Cylinder Zone 5 Temp. | 199 - 249 | °C | |
| Die Temperature | 199 - 249 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Note Message | |
|---|---|
| 1 . | Mouth die C, 510mm/min |
| 2 . | Mouth die C, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | C mold, 510mm/min |
| 6 . | Mouth die C, 510mm/min |
| 7 . | C mold, 510mm/min |
| 8 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ C15ST4 | Marplex Australia Pty. Ltd. | PP Copolymer | PROTEQ™ |
| THERMOLAST® K TC5GPN (Series: GP/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Ultramid® B3G10 SI | BASF Corporation | Nylon 6 | Ultramid® |
| Generic TPU-PC - Barium Sulfate | Generic | TPU-PC | Generic |
| Karina BLACK PVC COMPOUND 670-DA-48/1 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |