DOWLEX™ 2035G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gZgzaI_DOWLEX-2035G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ 2035G Polyethylene Resin is suitable for the production of cast films where low orientation in the film and ease of processing are primary considerations. Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.919 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Tensile Strength 1 | ASTM D882 | ||
| MD : Yield, 23 µm, extruded film | 7.00 | MPa | ASTM D882 |
| TD : Yield, 23 µm, extruded film | 7.00 | MPa | ASTM D882 |
| MD : Fracture, 23 µm, extruded film | 26.0 | MPa | ASTM D882 |
| TD : Fracture, 23 µm, extruded film | 20.0 | MPa | ASTM D882 |
| Tensile Elongation 2 | ASTM D882 | ||
| MD : Fracture, 23 µm, extruded film | 520 | % | ASTM D882 |
| TD : Fracture, 23 µm, extruded film | 690 | % | ASTM D882 |
| Dart Drop Impact 3(23 µm, Cast Film) | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength 4 | ASTM D1922 | ||
| MD : 23 µm, cast film | 250 | g | ASTM D1922 |
| TD : 23 µm, cast film | 490 | g | ASTM D1922 |
| Film tensile properties-load on pallets 5 | 13000 | g | ASTM D4649 |
| Film tensile properties-improve tear strength- @ Maximum stretch rate 6 | 47 | % | ASTM D4649 |
| Film Tensile Properties-Maximum Elongation 7 | 340 | % | ASTM D4649 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 97.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 8(20 °, 23.0 µm, cast film) | 148 | ASTM D2457 | |
| Haze 9(23.0 µm, Cast Film) | 0.70 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 280 | °C |
| Extrusion instructions |
|---|
| 铸造薄膜挤出的制造条件： 冷却辊温度：20 至 60°C。 熔体温度：220 至 280°C。 脱离速度：150 至 300 米/分。 建议的厚度范围：10 至 60 µm。 |
| Note Message | |
|---|---|
| 1 . | 150 m/min; Cooling roller 25 c. |
| 2 . | 150 m/min; Cooling roller 25 c. |
| 3 . | 150 m/min; Cooling roller 25 c. |
| 4 . | 150 m/min; Cooling roller 25 c. |
| 5 . | 23 µm cast film, 150 m/min, cooling roller 25°C. |
| 6 . | 23 µm cast film, 150 m/min, cooling roller 25°C. |
| 7 . | 23 µm cast film, 150 m/min, cooling roller 25°C. |
| 8 . | 150 m/min; Cooling roller 25 c. |
| 9 . | 150 m/min; Cooling roller 25 c. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SI302G15 | RJM International, Inc. | PET | RJM |
| AQUATUF® HM-337 (Comp) | Ravago Manufacturing Americas, LLC | HDPE | AQUATUF® |
| ISOPAK® 547 | Great Eastern Resins Industrial Co Ltd (GRECO) | ABS | ISOPAK® |
| POLIMAXX 2563LCXTA5 | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |
| Sylvin 4250-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |