NEMCON H PC/ABS DP182
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | NEMCON H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gZM7Ll_NEMCON-H-PC-ABS-DP182.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate/Acrylonitrile Butadiene Styrene, thermally and electrically conducting grade. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.69 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 | % | |
| Across Flow | 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 4880 | MPa | ASTM D638 |
| Tensile Strength 2(Break, 23°C) | 35.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 23°C) | 1.4 | % | ASTM D638 |
| Flexural Modulus 4(23°C, 50.0 mm Span) | 3690 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 23°C, 50.0 mm Span) | 57.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 19 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Conductivity | Internal Method | ||
| -- 6 | 0.80 to 1.1 | W/m/K | |
| -- 7 | 4.0 to 8.0 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Nozzle Temperature | 260 to 270 | °C | |
| Processing (Melt) Temp | 255 to 265 | °C | |
| Mold Temperature | 90.0 to 100 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.138 | MPa | |
| Screw Speed | 60 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Through Plane |
| 7 . | In Plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 381 TFE 10 EM | RTP Company | PC | RTP |
| SCHULAFORM® 9 B AR | A. Schulman Europe | Acetal (POM) Copolymer | SCHULAFORM® |
| Sylvin 8200-95UV Grey 9539 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Elastollan® 1185 A W | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| KOPEL® KP3855FB | Kolon Plastics, Inc. | TPEE | KOPEL® |