Ebalta AH 110 / TGL
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gZDgb9_Ebalta-AH-110-TGL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta AH 110 is an unfilled epoxy resin with high strength values and dimensional stability, even at increased temperature. It can be used as casting resin with powdered fillers as aluminium powder, laminating resin with glass fabric and binder with grainy fillers as aluminium granules. Depending on application the suitable hardener can be mixed with the resin. AH 110/TGL is suitable as laminating resin for big surfaces at a temperature range until 110°C. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 82 to 88 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 3000 to 3600 | MPa | ISO 178 |
| Flexural Stress | 125 to 145 | MPa | ISO 178 |
| Compressive Stress | 105 to 125 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 8.0 to 24 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 98.0 to 104 | °C | ISO 75-2/B |
| Glass Transition Temperature | 102 | °C | DSC |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 22 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Post Cure Time (80°C) | 12 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.11 to 1.15 | g/cm³ | |
| Viscosity (25°C) | 0.85 to 1.2 | Pa·s | |
| Curing Time (20°C) | 15 to 18 | hr | |
| Pot Life 1(20°C) | 55 to 65 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NAXALOY® 770 GF10 | MRC Polymers, Inc. | PC+ABS | NAXALOY® |
| Chemiton CSF0RA 75 | Franplast S.r.l. | SEBS | Chemiton |
| EstaGrip® ST 80A TPE | Lubrizol Advanced Materials, Inc. | TPU-Polyether | EstaGrip® |
| Hifax TKC220X 1 | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| Karina CLEAR PVC COMPOUND 40/205 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |