LNP™ VERTON™ RV00AES compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gZAXGE_LNPVERTONRV00AEScompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON* RV00AES is a compound based on PA 66 resin containing Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized. Also known as: LNP* VERTON* Compound RF-700-10 EM HS Product reorder name: RV00AES |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.58 | g/cm³ | ASTM D792 |
| -- | 1.60 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.18 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.22 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.80 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.30 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 9.8E-3 | % | ASTM D570 |
| 23°C, 24 hr | 0.90 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 17500 | MPa | ASTM D638 |
| -- | 17800 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 276 | MPa | ISO 527-2/5 |
| Fracture | 254 | MPa | ASTM D638 |
| Fracture | 265 | MPa | ISO 527-2 |
| Fracture | 276 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 2.0 | % | ISO 527-2/5 |
| Fracture | 1.9 | % | ASTM D638, ISO 527-2 |
| Fracture | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- | 14200 | MPa | ASTM D790 |
| -- | 15600 | MPa | ISO 178 |
| -- 2 | 15000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 374 | MPa | ASTM D790 |
| -- | 371 | MPa | ISO 178 |
| -- | 366 | MPa | ISO 178 |
| Flexural Strain at Break 3 | 3.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 380 | J/m | ASTM D256 |
| -40°C 4 | 39 | kJ/m² | ISO 180/1A |
| 23°C 5 | 45 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6(23°C) | 90 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 15.0 | J | ASTM D3763 |
| -- | 15.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 64.0mm span 7 | 259 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 241 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 8 | 256 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 110 | °C | UL 746 |
| RTI | 110 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 288 - 299 | °C | |
| Processing (Melt) Temp | 288 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 mm |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PC GN1007FM | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| Americas Styrenics MC3700 | Americas Styrenics LLC | PS (GPPS) | Americas Styrenics |
| CompaDur® 151 black (020) | DimeLika Plast GmbH | PBT | CompaDur® |
| INLUBE PPSTF18SI2 | Infinity LTL Engineered Compounds | PPS | INLUBE |
| SQUARE® LIM8633-60A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |