ISPLEN® PR210 G4E
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ISPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gYuXXI_ISPLENPR210G4E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ISPLEN® PR210G4E is a random ethylene-propylene copolymer with a high molecular weight. It contains a basic antioxidant stabilization for the pipe extrusion that guarantees the stability of the polymer under normal processing. The additives used are compatible with any others that the customer might wish to add. ISPLEN® PR210G4E is supplied in natural colour. TYPICAL APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 0.30 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 1.2 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 26.0 | MPa | ISO 527-2 |
| Fracture | 27.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 520 | % | ISO 527-2 |
| Flexural Modulus | 815 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | > 9.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 45.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 70.0 | °C | ISO 306/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP161T | Southern Polymer, Inc. | PP Homopolymer | PRIMALENE |
| WPP PP PPC2TF2HS-Natural | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| Borstar® ME3407 | Borealis AG | MDPE | Borstar® |
| LNP™ LUBRICOMP™ OL003A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ LUBRICOMP™ |
| Wanthane® WHT-1185F | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |