Generic Plastomer
| Category: | Plastomer , Ethylene-based Plastomer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gYbgwn_Generic-Plastomer.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Plastomer This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.880 to 0.921 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 0.50 to 10 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 0.80 to 30 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (23°C) | 978 to 1000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (23°C) | 26 to 85 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 12.8 to 23.7 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 490 to 510 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 22.0 to 112 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| MD | 54.5 to 152 | MPa | |
| TD | 34.3 to 172 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 3.45 to 6.25 | MPa | |
| TD : Yield | 4.05 to 4.56 | MPa | |
| MD : Break | 35.0 to 78.9 | MPa | |
| TD : Break | 31.6 to 73.9 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield | 9.0 to 14 | % | |
| TD : Yield | 7.2 to 11 | % | |
| MD : Break | 9.7 to 750 | % | |
| TD : Break | 600 to 1200 | % | |
| Dart Drop Impact (23°C) | 22 to 1300 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 44 to 300 | g | |
| TD | 220 to 650 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 55.8 to 83.1 | °C | ASTM D1525 |
| -- | 38.0 to 97.2 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 73.0 to 97.6 | °C | ISO 11357-3 |
| -- | 57.7 to 109 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 54 to 94 | ASTM D2457 | |
| Haze | 0.30 to 2.5 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS ZF5551 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Sylvin 7015 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Advanced-PP 1104K | Advanced Petrochemical Company | PP Homopolymer | Advanced-PP |
| Celanex® 2104UV | Celanese Corporation | PBT | Celanex® |
| Optix® CA-61 | Plaskolite West, Inc. | Acrylic (PMMA) | Optix® |