VALOX™ 325FC resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gY9ayw_VALOX325FCresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Commercial, VALOX 325FC is compliant with food contact regulations. VALOX 325FC is a general purpose, unreinforced PBT injection moulding resin which contains internal mold release. This new 325FC grade is a good processable resin that exhibits faster and more economical cycle times. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/2.16 kg | 20.0 | cm³/10min | ISO 1133 |
| 250°C/5.0 kg | 50.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | Internal method | ||
| Flow | 2.0 - 2.6 | % | Internal method |
| Transverse flow | 0.90 - 1.8 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.34 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 145 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2500 | MPa | ASTM D638 |
| -- | 2550 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Fracture 4 | 60.0 | MPa | ASTM D638 |
| Fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 7.0 | % | ASTM D638 |
| Yield | 10 | % | ISO 527-2/50 |
| Fracture 6 | 15 | % | ASTM D638 |
| Fracture | 15 | % | ISO 527-2/50 |
| Flexural Modulus 7 | 2400 | MPa | ISO 178 |
| Flexural Stress | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30°C | 4.0 | kJ/m² | ISO 179/2C |
| 23°C | 4.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | ISO 179/2U | ||
| -30°C | 80 | kJ/m² | ISO 179/2U |
| 23°C | No Break | ISO 179/2U | |
| Notched Izod Impact | |||
| -30°C | 36 | J/m | ASTM D256 |
| 0°C | 36 | J/m | ASTM D256 |
| 23°C | 38 | J/m | ASTM D256 |
| -30°C 8 | 4.0 | kJ/m² | ISO 180/1A |
| 0°C 9 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 10 | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | No Break | ASTM D4812 | |
| 23°C | No Break | ASTM D4812, ISO 180/1U | |
| -30°C 11 | 100 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 12 | |||
| 0.45 MPa, unannealed, 64.0mm span | 150 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 50.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 185 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 13 |
| -- | 220 | °C | ASTM D1525, ISO 306/A50 10 14 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 165 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 - 60.0 | °C | |
| Rear Temperature | 230 - 245 | °C | |
| Middle Temperature | 240 - 255 | °C | |
| Front Temperature | 245 - 265 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 50 mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| 14 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 400 GB 20 | RTP Company | PS (GPPS) | RTP |
| ACCUTECH™ HP0336C40L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| GAPEX® RPP20EU32UL | Ferro Corporation | PP, Unspecified | GAPEX® |
| Electroblend® PP-1805 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP Homopolymer | Electroblend® |
| CP PRYME® Polypropylene PPC100/2I-20M NAT | Chase Plastics Services Inc. | PP Copolymer | CP PRYME® Polypropylene |