Order Products : sales@su-jiao.com
XANTAR® F 25 R
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | XANTAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gXaedX_XANTAR-F-25-R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Viscosity, Flame Retardant, Molding Release |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.60 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.35 | % | ISO 62 |
| Limiting Viscosity Number | 56.0 | cm³/g | ISO 1628-4 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Conductivity of Melt | 0.24 | W/m/K |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 70 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 80 | kJ/m² | ISO 180/4A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 130 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | UL 746 | ||
| 1.50 mm | 130 | °C | |
| 3.00 mm | 130 | °C | |
| RTI Imp | UL 746 | ||
| 1.50 mm | 125 | °C | |
| 3.00 mm | 125 | °C | |
| RTI Str | UL 746 | ||
| 1.50 mm | 125 | °C | |
| 3.00 mm | 130 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 29 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.00 | ||
| 1 MHz | 2.90 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 6.6E-4 | ||
| 1 MHz | 9.2E-3 | ||
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 3.00 mm | V-0 | ||
| 1.50 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 850 | °C | |
| 3.00 mm | 850 | °C | |
| Oxygen Index | 35 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 89.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA1212 PA1212C-02 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| Styrolution PS 6200/6201 | INEOS Styrolution Group GmbH | PS (HIPS) | Styrolution PS |
| Trademark PP PPC150E | Trademark Plastics Corporation | PP Impact Copolymer | Trademark PP |
| Yanshan PE LD104 | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| Karina BLACK PVC COMPOUND -E 851-48/ 1-F-ISM (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |