Telcar® TL-1000-92-UV
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Telcar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gXALIR_Telcar-TL-1000-92-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Telcar®TL-1000-92-UV is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Typical application areas include:
|
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 180°C, 30 minutes | 1.3 | % | ASTM D955 |
| 24 hours | 1.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 10 sec) | 42 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 290 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% strain | 8.41 | MPa | ASTM D412 |
| 300% strain | 8.55 | MPa | ASTM D412 |
| Tensile Strength | ASTM D412 | ||
| Yield 2 | 10.3 | MPa | ASTM D412 |
| Yield 3 | 7.58 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Yield 4 | 16 | % | ASTM D412 |
| Fracture 5 | 550 | % | ASTM D412 |
| Fracture 6 | 140 | % | ASTM D412 |
| Tear Strength 7 | 364 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (-40°C) | No Break | ASTM D256 | |
| Dart Drop Impact (-30°C) | 33.9 | J | ASTM D3029 |
| Tensile Impact Strength | 471 | kJ/m² | ASTM D1822 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | ASTM D573 | ||
| -- | 6.0 | % | ASTM D573 |
| 110°C, 1008 hr | 10 | % | ASTM D573 |
| 121°C, 1008 hr | 7.0 | % | ASTM D573 |
| Change in Ultimate Elongation in Air | ASTM D573 | ||
| 110°C, 1008 hr | -67 | % | ASTM D573 |
| 121°C, 1008 hr | -63 | % | ASTM D573 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 62.5 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 40.7 | °C | ASTM D648 |
| Glass Transition Temperature | -55.9 | °C | ASTM E1356 |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 30 | mm/min | ISO 3795 |
| Additional Information |
|---|
| 装有测量仪表的屈服落镖冲击能量，-40°C，9000 英寸/分钟，韧性破坏：200 英寸-磅装有测量仪表的断裂落镖冲击能量，-40°C，9000 英寸/分钟，韧性破坏：1359密耳装有测量仪表的断裂落镖冲击能量，-40°C，9000 英寸/分钟，韧性破坏：350英寸-磅雾化，Kaake Buchler，3小时，100°C：92撕裂强度，ASTM D1004，C型铸：364 磅/英寸热老化性能伊佐德冲击，1000小时，120°C：无断裂拉伸冲击强度，ASTM D1822：>>224 英尺-磅/平方英寸可燃性燃烧速率，FMVSS 302，最大100，30.2毫米/分钟：合格可燃性，燃烧速率，FMVSS 302，最大100，1.2英寸/分钟：合格 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 193 | °C | |
| Middle Temperature | 177 - 199 | °C | |
| Front Temperature | 182 - 204 | °C | |
| Nozzle Temperature | 188 - 210 | °C | |
| Processing (Melt) Temp | 188 - 210 | °C | |
| Mold Temperature | 25.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 166 - 188 | °C | |
| Cylinder Zone 2 Temp. | 171 - 193 | °C | |
| Cylinder Zone 3 Temp. | 177 - 199 | °C | |
| Cylinder Zone 5 Temp. | 182 - 204 | °C | |
| Die Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | Type 1, 510mm/min |
| 4 . | Type 1, 510mm/min |
| 5 . | 51 mm/min |
| 6 . | 510 mm/min |
| 7 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULINK® XL 351 | A. Schulman Inc. | XLPE | SCHULINK® |
| Celcon® MR25B | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Lucolit® 1320 | Lucobit AG | TPO (POE) | Lucolit® |
| PERCOM® KMG40W | A. Schulman Europe | PP Copolymer | PERCOM® |
| Sylvin 6185-80 Grey 9166 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |