G-PAEK™ 1230GF
| Category: | PEK , Polyether Ketone |
| Manufacturer: | Gharda Chemicals Ltd. |
| Trademark: | G-PAEK™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gWvfI4_G-PAEK-1230GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Details: Ultra high performance thermoplastic polymer, 30% glass fiber reinforced in Polyether Ketone, semi-crystalline granules suitable for injection molding, easy flow, Beige in color. Application Areas: Suitable for high temperature applications, where higher strength in load-bearing applications is required. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | |
| Spiral Flow 1 | 3.10 | cm | ASTM D3123 |
| Molding Shrinkage 2 | |||
| Flow | 0.30 | % | |
| Across Flow | 1.0 | % | |
| Water Absorption (Equilibrium) | 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 92 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11500 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 185 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.0 to 3.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 10500 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 280 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 60 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 610 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 358 | °C | ASTM D648 |
| Continuous Use Temperature | 280 | °C | UL 746B |
| Glass Transition Temperature | 152 | °C | ASTM D3418 |
| Melting Temperature | 372 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm) | 20 | kV/mm | ASTM D149 |
| Arc Resistance 3 | 160 | sec | ASTM D495 |
| Comparative Tracking Index 4 | 140 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Nozzle Temperature | 420 | °C | |
| Processing (Melt) Temp | 390 to 420 | °C | |
| Mold Temperature | 200 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 420°C nozzle, 220°C Mold |
| 2 . | 420°C nozzle, 220°C Mold |
| 3 . | 500 V |
| 4 . | 50 drops |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 19HT40-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| CYCOLOY™ CM8622 resin | SABIC Innovative Plastics Europe | PC+ABS | CYCOLOY™ |
| Epiall® 1904B-1 | Sumitomo Bakelite North America, Inc. | Epoxy | Epiall® |
| Huafon JF-W-AH6140 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Sylvin 2999-67LG Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |