Hapsil™ 360
| Category: | Rubber , Rubber |
| Manufacturer: | Hapco Inc. |
| Trademark: | Hapsil™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gWtdvv_Hapsil-360.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hapsil 360 is a high tear strength, tin-catalyzed RTV-2 silicone rubber, which was designed for casting Hapco's wide variety of rigid and flexible polyurethane resins. Hapsil 360 is not sensitive to inhibition, meaning it will cure at room temperature over virtually any surface. Hapsil 360 works well with clear and colorless casting resins that typically exhibit a sticky, uncured surface when cast against most silicones. It is easy to mix and de-air, and cures with minimal shrinkage. Hapsil 360 can be used with or without a release agent and is ideal for any application where a strong flexible rubber is required. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.70 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 27 to 33 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 2.93 to 3.28 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 400 to 450 | % | ASTM D412 |
| Tear Strength 2 | 17.5 to 26.3 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | -34 to 177 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 5.0, Mix Ratio by Volume: 5.6 | ||
| Thermoset Mix Viscosity 3(25°C) | 3450 to 3550 | cP | ASTM D2393 |
| Demold Time (21°C) | 60 to 180 | min | Internal Method |
| Post Cure Time (50°C) | 6.0 to 8.0 | hr |
| Note Message | |
|---|---|
| 1 . | Mixed |
| 2 . | Die C |
| 3 . | Mixed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PONYL 4003EPG20 | POLYROCKS CHEMICAL CO., LTD | Nylon 66 | PONYL |
| TEKNIFLEX® PXA 1060 | Tekni-Films, a div of Tekni-Plex | Film, Copolyester/PCTFE | TEKNIFLEX® |
| Next Nylon 66 Prime Series PG30-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Cytec XMTM54FRB | Cytec Industries Inc. | Epoxy | Cytec |
| Iupilon® DS3002R 7051A | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |