Next PC CX-01WH
| Category: | PC , Polycarbonate |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gWt1c6_Next-PC-CX-01WH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PC UnFilled White Compound Product Applications Electrical/Electronics, Housing Appliance, Industrial, Medical & health care application such as Telecommunication hardware, sunroom, carports, car & truck washes, LCD, sliding doors, window, lab Instrument etc Benefits Good dimensional stability & High heat resistance |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | |
| Across Flow | 0.50 | % | |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.30 | % | |
| Saturation 1 | 0.35 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ASTM D638 |
| Tensile Strength | 64.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 60 | % | ASTM D638 |
| Flexural Modulus | 2200 | MPa | ASTM D790 |
| Flexural Strength | 93.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) | ASTM D256 | ||
| -30°C | 11.0 | kJ/m² | |
| 23°C | 60.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 136 | °C | |
| 1.8 MPa, Unannealed | 125 | °C | |
| Vicat Softening Temperature | 140 | °C | ASTM D1525 |
| CLTE - Flow (23 to 80°C) | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 27 | kV/mm | IEC 60243-1 |
| Dielectric Constant (60 Hz) | 3.00 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 270 to 280 | °C | |
| Middle Temperature | 280 to 290 | °C | |
| Front Temperature | 290 to 300 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 1007 | Chevron Phillips Chemical Company LLC | LDPE | Marlex® |
| Vipel® F701-ABK-15 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| Wellamid® MR410 42H-NBK1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| PLUSTEK RA307G4 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| SQUARE® LIM3600-40A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |