UR, PBT+PC alloy. Outstanding low temperature impact/chemical resistance. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Specific Volume | 0.856 | cm³/g | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 to 1.2 | % | Internal Method |
| Water Absorption (24 hr) | 0.13 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 49.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 170 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 1720 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 530 | J/m | |
| 23°C | 800 | J/m | |
| Unnotched Izod Impact (23°C) | 3200 | J/m | ASTM D4812 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Energy at Peak Load | 55.9 | J | |
| 23°C, Energy at Peak Load | 48.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 116 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 96.1 | °C | |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI Str | 75.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 9.5E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Air | 29 | kV/mm | |
| 3.20 mm, in Air | 20 | kV/mm | |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 2.93 | ||
| 1 MHz | 2.95 | ||
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 2.0E-3 | ||
| 1 MHz | 0.030 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 to 80 | % | |
| Rear Temperature | 243 to 266 | °C | |
| Middle Temperature | 249 to 271 | °C | |
| Front Temperature | 254 to 277 | °C | |
| Nozzle Temperature | 254 to 271 | °C | |
| Processing (Melt) Temp | 260 to 277 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.013 to 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD A 2800 B-75A Black | RTP Company | TPO (POE) | RTP |
| RheTech Polypropylene T40P100-774UVA | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| REPOL® R019MG | Reliance Industries Limited | PP Random Copolymer | REPOL® |
| Stanyl® TC154 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Hapcoat™ 3721LV | Hapco Inc. | TP, Unspecified | Hapcoat™ |