Reny® 4501 is a Polyarylamide (PARA) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Reny® 4501 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.66 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.10 kg) | 10 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.10 kg) | 7.50 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.060 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.80 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 20400 | 16200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 107 | 113 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.70 | 0.90 | % | ISO 527-2 |
| Flexural Modulus | 19100 | 15500 | MPa | ISO 178 |
| Flexural Stress | 190 | 184 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.5 | 6.6 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 14 | 15 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 236 | 232 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 225 | 216 | °C | ISO 75-2/A |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 265 | °C | |
| Front Temperature | 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer Z70B | Precision Polymer Engineering Ltd. | NBR | Precision Polymer |
| Sinvicomp SRF3705ZE | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Sinpolene HFR8124 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinpolene |
| Niuk 40RN00 | Shanghai Niuk New Plastic Technology Co., Ltd. | Nylon 6 | Niuk |
| Evermore PUR B-666NC | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |