KIBILAC® PW-997L
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | KIBILAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gW2S1t_KIBILAC-PW-997L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Matting ASA features and benefits:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 6.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 44.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 35 | % | ASTM D638 |
| Flexural Modulus 3 | 2210 | MPa | ASTM D790 |
| Flexural Strength 4 | 68.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 110 | °C | ASTM D1525 5 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 20 | ASTM D523 |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 6.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS-301ML | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| XIRAN® SG240 | Polyscope Polymers BV | SMA | XIRAN® |
| APEX® 90-A481R-80-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Karina CLEAR PVC COMPOUND -E 800/208-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina IVORY PVC COMPOUND -E 105900-35/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |