LNP™ LUBRICOMP™ WL001RZ compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gVvMpN_LNP-LUBRICOMP-WL001RZ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP WL001RZ is a compound based on PBT containing Propietary Filler(s). Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound WL001RZ Product reorder name: WL001RZ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.34 | g/cm³ | |
| -- | 1.33 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 to 4.0 | % | |
| Across Flow : 24 hr | 2.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.070 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.13 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2690 | MPa | ASTM D638 |
| -- | 2660 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 53.0 | MPa | ISO 527-2/5 |
| Break 2 | 54.0 | MPa | ASTM D638 |
| Break | 52.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 10 | % | ISO 527-2/5 |
| Break 3 | 9.0 | % | ASTM D638 |
| Break | 15 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 2570 | MPa | ASTM D790 |
| -- 5 | 2450 | MPa | ISO 178 |
| Flexural Stress | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 6 | 4.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 840 | J/m | ASTM D4812 |
| 23°C 7 | 52 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 3.90 | J | ASTM D3763 |
| -- | 1.04 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 183 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 8 | 143 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 65.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 55.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 8.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.7E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wondel® P PN0T | Nanjing Julong Engineering Plastics Co., LTD | PP, Unspecified | Wondel® P |
| Mylar® A (200 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Badamid® PA12 GM30 H S2 | Bada AG | Nylon 12 | Badamid® |
| Expandable PS D833B | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| 3M™ Dyneon™ PTFE Compound TF 3215S | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |