Geon™ HTX L1502
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ HTX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gVsQrl_Geon-HTX-L1502.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Geon™HTX L1502 is a polyvinyl chloride alloy (PVC alloy) product,. It can be processed by extrusion and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: architectural applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 12445 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 78 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2720 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 48.9 | MPa | ASTM D638 |
| Flexural Modulus | 2970 | MPa | ASTM D790 |
| Flexural Strength | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 51 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 57.8 | J/cm | ASTM D4226 |
| 23°C 4 | 57.8 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, annealed, 3.18mm 5 | 88.3 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm 6 | 83.9 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm 7 | 82.8 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm 8 | 85.4 | °C | ASTM D648 |
| CLTE - Flow | 6.6E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Physical properties based on Geon HTX L1502 white 1000. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 193 - 204 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Procedure A, C.125 Throwing |
| 4 . | Procedure B, C.125 Throwing |
| 5 . | Annealed at 50 deg.C |
| 6 . | Annealed at 60 deg.C |
| 7 . | Annealed at 50 deg.C |
| 8 . | Annealed at 60 deg.C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® RX®2-501N | Vyncolit N.V. | DAP | Vyncolit® |
| Boda BDP-K7702 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| TechnoFiber Performance PP LGF 20-10-02 HI | TechnoCompound GmbH | PP, Unspecified | TechnoFiber Performance |
| ICORENE® 5045 SL | A. Schulman Europe | HDPE | ICORENE® |
| LNP™ LUBRICOMP™ GFL36L compound | SABIC Innovative Plastics | PSU | LNP™ LUBRICOMP™ |