Bayflex® 952
| Category: | PUR-MDI , Polyurethane (MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Bayflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gVAV77_Bayflex-952.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bayflex 952 is a fully compounded polyether-based polyurethane system consisting of two liquid components which can be water-blown. Component A is a modified diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system. The Bayflex 952 system is used in the manufacture of microcellular polyurethane shoe soles. Soles prepared from these components combine light weight, comfort, and durability. Processibility and dynamic flexural properties are excellent over a wide range of densities. The combination of excellent physical properties and ease of processing has made the Bayflex 952 system a prime soling material for single-density soles for fashion and casual shoes. As with any product, use of the Bayflex 952 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.500 | g/cm³ | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 70.0 | mg | ASTM D4060 |
| Ross Flex - 0% Cut Growth | ASTM D1052 | ||
| -29°C, 6.35 mm | > 5.0E+4 | Cycles | ASTM D1052 |
| 23°C, 6.35 mm | > 1.0E+5 | Cycles | ASTM D1052 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oil Resistance - Volume Swell | % | ASTM D5694 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 3.10 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 400 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 4.38 | kN/m | Internal method |
| -- 2 | 14.0 | kN/m | ASTM D1004 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components 3 | |||
| Component a | Mixing ratio by weight: 70 | ||
| Component B | Mixing ratio by weight: 100 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Part A Type: Isocyanate Appearance: Light yellow viscous liquid Specific Gravity @ 25°C: 1.20 Viscosity @25°C: 1100 mPa Flash Point, PMCC: 207°C NCO: 18.7 to 19.1 wt% Bulk Density at 25°C: 10.01 lb/gal Part B Type: Polyol Appearance: White liquid Specific Gravity @ 25°C: 1.05 Viscosity @25°C: 1100 mPa-s Flash Point, PMCC: 138°C Bulk Density at 25°C: 8.70 lb/gal Water: 0.38 wt% max Hydroxyl Number: 157 Material Temperature: 28°CMold Temperature: 49°CDemold Time: 3.5 minLinear Shrinkage at 0.50 g/cm³: <1.0%Hand Mix Reactivity at 25°C Cream Time: 10 to 18 sec Tack-Free Time: 30 to 45 sec Pull Time: 40 to 55 sec Free-Rise Density: 15 to 18 lb/ft³ |
| Note Message | |
|---|---|
| 1 . | Block |
| 2 . | C mould |
| 3 . | 98 Index |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makropol® PC A3 G20 PRTA010 PC315 | Petropol Industry and Trade of Polymers LTDA | PC | Makropol® PC |
| UNIPA® M | Nytef Plastics, Ltd. | Nylon 6 | UNIPA® |
| NuSil MED-4801 | NuSil Technology | Silicone Rubber, LSR | NuSil |
| INSTRUC PCABSGF20 | Infinity LTL Engineered Compounds | PC+ABS | INSTRUC |
| LEXAN™ 3414R resin | SABIC Innovative Plastics | PC | LEXAN™ |