LG ABS RS650

Category:	ABS , Acrylonitrile Butadiene Styrene
Manufacturer:	LG Chem Ltd.
Trademark:	LG ABS
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	gUikNc_LG-ABS-RS650.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

LG ABS RS650 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is extrusion.

The main features of LG ABS RS650 are:

flame retardant/rated flame

ROHS certification

General Information
Features	General
Uses	General
RoHS Compliance	RoHS compliance
Processing Method	Extrusion
Multi-Point Data	Specific Heat vs. Temperature (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--	1.04	g/cm³	ASTM D792
--	1070	kg/m³	ISO 1183 ¹
Melt Mass-Flow Rate (MFR) (220°C/10.0 kg)	6.5	g/10 min	ASTM D1238
Melt volume-flow rate (220°C/10.0 kg)	7.00	cm³/10min	ISO 1133 ²
Molding Shrinkage - Flow (3.20 mm)	0.40 - 0.70	%	ASTM D955
Water Absorption (Saturation)	0.19	%	ISO 62 ³

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	107		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2500	MPa	ISO 527-2 ⁴
Tensile Strength
Yield, 3.20mm ⁵	49.0	MPa	ASTM D638
Yield	44.0	MPa	ISO 527-2 ⁶
Tensile Elongation
Yield, 3.20mm ⁷	> 5.0	%	ASTM D638
Yield	5.0	%	ISO 527-2 ⁸
Fracture, 3.20mm ⁹	35	%	ASTM D638
Tensile Elongation at Break	20	%	ISO 527-2 ¹⁰
Flexural Modulus ¹¹(3.20 mm)	2550	MPa	ASTM D790
Flexural Strength ¹²(3.20 mm)	80.4	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA ¹³
-30°C	12.4	kJ/m²	ISO 179/1eA
23°C	30.0	kJ/m²	ISO 179/1eA
Charpy impact strength			ISO 179/1eU ¹⁴
-30°C	56.2	kJ/m²	ISO 179/1eU
23°C	No Break		ISO 179/1eU
Notched Izod Impact			ASTM D256
23°C, 3.20 mm	320	J/m	ASTM D256
23°C, 6.40 mm	290	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, unannealed, 6.40mm	95.0	°C	ASTM D648
1.8 MPa, unannealed, 6.40mm	87.0	°C	ASTM D648
Glass Transition Temperature ¹⁵	110	°C	ISO 11357-2 ¹⁶
Vicat Softening Temperature
--	95.0	°C	ASTM D1525 ¹⁷
50°C/h, B (50N)	95.8	°C	ISO 306 ¹⁸
Linear expansion coefficient			ISO 11359-2 ¹⁹
Flow	8.0E-5	cm/cm/°C	ISO 11359-2
Lateral	9.1E-5	cm/cm/°C	ISO 11359-2
RTI Elec			UL 746
1.50 mm	60.0	°C	UL 746
3.00 mm	60.0	°C	UL 746
RTI Imp			UL 746
1.50 mm	60.0	°C	UL 746
3.00 mm	60.0	°C	UL 746
RTI			UL 746
1.50 mm	60.0	°C	UL 746
3.00 mm	60.0	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+15	ohms	IEC 60093 ²⁰
Volume Resistivity
--	1.0E+16	ohms·cm	IEC 60093
--	> 1.0E+13	ohms·m	IEC 60093 ²¹
Dielectric Strength
--	37	kV/mm	IEC 60243-1
--	47	kV/mm	IEC 60243-1 ²²
Arc Resistance	PLC 6		ASTM D495
Comparative Tracking Index (CTI)	PLC 0		UL 746
Comparative Tracking Index	525		IEC 60112 ²³
High Amp Arc Ignition (HAI)			UL 746
1.50 mm	PLC 0		UL 746
3.00 mm	PLC 0		UL 746
High Voltage Arc Tracking Rate (HVTR)	PLC 1		UL 746
Hot-wire Ignition (HWI)			UL 746
1.50 mm	PLC 4		UL 746
3.00 mm	PLC 4		UL 746

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
1.50 mm, NC, WT, BK	HB		UL 94
3.00 mm, NC, WT, BK	HB		UL 94
Burning Behav. at thickness h (3.20 mm, UL)	HB		ISO 1210 ²⁴

Extrusion	Nominal Value	Unit
Drying Temperature	70.0 - 80.0	°C
Drying Time	3.0 - 4.0	hr
Cylinder Zone 1 Temp.	180 - 210	°C
Cylinder Zone 2 Temp.	190 - 230	°C
Cylinder Zone 3 Temp.	200 - 250	°C
Cylinder Zone 4 Temp.	200 - 250	°C
Adapter Temperature	200 - 250	°C
Melt Temperature	200 - 250	°C
Die Temperature	200 - 250	°C

Extrusion instructions
Minimum Moisture Content: 0.01%Roll Stack Temperature, Top: 70 to 100°CRoll Stack Temperature, Middle: 70 to 90°CRoll Stack Temperature, Bottom: 60 to 90°C

Note Message
1 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
2 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
3 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
4 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
5 .	50 mm/min
6 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
7 .	50 mm/min
8 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
9 .	50 mm/min
10 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
11 .	15 mm/min
12 .	15 mm/min
13 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
14 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
15 .	10 °C/min
16 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
17 .	速率 A (50°C/h), 载荷2 (50N)
18 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
19 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
20 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
21 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
22 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
23 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
24 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???

Resin Grade	Manufacturer	Category	Trademark
Sinpolene MBW1444	Teknor Apex Asia Pacific PTE. LTD.	PP, Unspecified	Sinpolene
Spartech Polycom PP5230F B1	Spartech Polycom	PP, Unspecified	Spartech
GLS Nylon 6 PN09(E)	GLS Polymers Pvt. Ltd.	Nylon 6	GLS Nylon 6
Hostaform® S 27064 XAP² ™	Celanese Corporation	Acetal (POM) Copolymer	Hostaform®
LEXAN™ HFD4471 resin	SABIC Innovative Plastics	PC	LEXAN™