| Unreinforced, UV Stabilized, Polyamide 66 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.3 | -- | % | |
| Flow | 1.3 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 8.5 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.7 | -- | % | |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3200 | 1500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 85.0 | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.3 | 25 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 24 | > 50 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 1340 | MPa | |
| 1000 hr | -- | 600 | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | 3.0 | kJ/m² | |
| 23°C | 6.0 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 55 | 55 | kJ/m² | |
| 23°C | 45 kJ/m² | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 4.0 | 3.0 | kJ/m² | |
| 23°C | 5.0 | 12 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 205 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 60.0 | -- | °C | ISO 11357-2 |
| Vicat Softening Temperature | 240 | -- | °C | ISO 306/B50 |
| Melting Temperature 2 | 263 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.0E-4 | -- | cm/cm/°C | |
| Transverse | 1.1E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.710 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| Oxygen Index | 27 | -- | % | ISO 4589-2 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Emission of Organic Compounds | 6.60 | -- | µgC/g | VDA 277 |
| Odor | 2.5 | -- | VDA 270 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoFlo 30A-300 | KMI Group Inc. | SEBS | PrimoFlo |
| Silmar® SIL93BE-1122B | Interplastic Corporation | Polyester, TS | Silmar® |
| CompaMid® PA 6.6 GF 30 | DimeLika Plast GmbH | Nylon 66 | CompaMid® |
| DIC.PPS FZ-3600-D5 | DIC Corporation | PPS | DIC.PPS |
| Lighter™ S93 | Equipolymers | PET | Lighter™ |