KOPELEN SB-550A
| Category: | PP Terpolymer , Polypropylene Terpolymer |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | KOPELEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gUGOv1_KOPELEN-SB-550A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SB-550A is random terpolymer polypropylene for injection blow molding with good transparency and good gloss. This product is designed to be processed by Injection or injection stretch blow molding application. SB-550A offers very high clarity, flexible stiffness and chemical resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 24.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 834 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 90.0 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 20 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTOUGH RZ320G2/RZ321G2 | Polyram Ram-On Industries | PC | RAMTOUGH |
| AKROMID® B3 GF 15 black (4002) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Escorene™ Ultra LD 728.61 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| LUVOCOM® NSB 90 NT | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Sylvin 9077-60 Yellow 4126 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |