Infino HP-1011
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gThf0I_Infino-HP-1011.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Material with superior flowability and small gas generation that can be applied to the exterior material of mobile phone |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 35 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 49.0 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2/50 |
| Break | 48.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 92 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 1800 | MPa | ASTM D790 |
| -- 3 | 1910 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 69.0 | MPa | ASTM D790 |
| -- 5 | 68.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 56 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 590 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 460 | J/m | ASTM D256 |
| 23°C 7 | 50 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 122 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 123 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 109 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 99.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 105 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 122 | °C | ISO 306/B50 |
| -- | 124 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 98.1 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| 7 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 9503H | Chevron Phillips Chemical Company LLC | HDPE, HMW | Marlex® |
| Maxelast® P1970 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| DURACON® TF-30 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer+PUR | DURACON® |
| INEOS LDPE 22D730 | INEOS Olefins & Polymers Europe | LDPE | INEOS LDPE |
| EPALINE 392A55 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPALINE |