Syncure™ System S120NA
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Syncure™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gTGGfy_Syncure-System-S120NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This product is used in applications requiring high density, high hardness or high temperature resistance (up to 125°C). |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.948 | g/cm³ | ASTM D792 |
| Gel Content 1 | 72 | % | ASTM D2765 |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Tensile strength retention rate 2(121°C, 1.91 mm) | 75 | % | |
| Elongation retention rate 3(121°C, 1.91 mm) | 75 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deformation 4(131°C) | 10 | % | UL 1581 |
| Thermal creep elongation 5 | 30 | % | |
| Oxidation Induction Time | 40 | min | ASTM D3895 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Catalyst parent mixture- S-1037B 6 | 5.0 | % | |
| Transplant-based resin- S1016A | 95 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 64 | ASTM D2240 | |
| Shaw D, 10 seconds | 59 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 7(Yield) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation 8(Break) | 80 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| UL Temperature Rating | 125 | °C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 2.10 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 2.0E-3 | ASTM D150 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| 注释：以上情况代表了在30密耳壁的14 AWG上测量得出的典型属性。存放和搬运：包装打开之后应在48小时之内使用，避免自硬化和报废。 |
| Note Message | |
|---|---|
| 1 . | Cross-linked PE, Method B (Non-Arbitration Test) |
| 2 . | 336 hours, UL standard |
| 3 . | 336 hours, UL standard |
| 4 . | 500g,1 hour |
| 5 . | SYV-40 |
| 6 . | S-1037B |
| 7 . | Type 4, 510mm/min |
| 8 . | Type 4, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 34S5201 | The Matrixx Group, Inc. | PBT | Matrixx |
| Styropor® BFL 495 | BASF Corporation | PS (EPS) | Styropor® |
| Nipol® LX531B | Zeon Corporation | Latex | Nipol® |
| HiFill® PA6/6 LGF50 2000 12mm | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Hoffman PVC V0-072x1 CLEAR | Hoffman Plastic Compounds Inc. | PVC, Flexible | Hoffman PVC |